Descriptiontranslated from Chinese
FIELD
The present invention relates to a galvanized steel wire, in particular, it relates to a high corrosion resistance coating treatment method of hot galvanized steel wire. A metallic metallurgical art.
Background technique
Zinc surface of galvanized steel by easily oxidized in air, poor corrosion resistance. Prone to white rust after a short period galvanizing surface, prone to red rust after a long time. Effect of quality of its appearance and corrosion resistance. For this reason, after the foreign-plated galvanized steel wire after completion of the stretching, a liquid-impregnated with an aqueous solution of hexavalent chromium and acidified (anhydrous chromic acid: sulfuric acid = 1:2.5:5:1:: nitric acid) in , then placing the air, and finally dried by heating, the hot galvanized steel surface hexavalent chromic acid rapidly form a dense film.
The reaction mechanism for the formation of hexavalent chromic acid coating: hot dipping galvanized steel, zinc dissolved in the solution acidified to hexavalent chromium, chromic acid reduction to produce the acid aqueous trivalent chromium compound as a main component in the surface coating of zinc precipitate, chromate coating formation. Reaction the following steps: 1) dissolution reaction of zinc: 2) chromic acid reduction reaction: 3) After this reaction, the galvanized layer surface PH value rise, precipitation of chromium acidified water:
4) Water is then acidified with chromium chromate and then reacting:
5) water with an acid to generate an acid group hexavalent mesh structure: 6) after hot air drying, shrinking film hexavalent chromic acid reaction, the precipitated zinc surface, forming the anticorrosive film.
Hexavalent chromic acid oxidation barrier film may be formed in contact with the layer of pure zinc oxyntomodulin to protect zinc, then there is enough iron to form zinc to protect the steel substrate potential, thereby further improving the corrosion resistance of galvanized steel wire, but also has excellent conductivity and coating with self-healing capabilities. However, due to the carcinogenic hexavalent chromium, hexavalent chromium acid film, and was banned around the world.
SUMMARY
Object of the present invention is to overcome the above disadvantages, there is provided a can enhance the corrosion resistance of galvanized steel wire, and a regeneration performance of the film, nor carcinogenic high corrosion resistance hot dip galvanized steel wire coating treatment method.
Object of the present invention is implemented as follows: A high-corrosion coating treatment method of hot galvanized steel, which is characterized in that it is hot dip galvanized steel wire after drawing the line after the end of the plate, washed with water, immersed in dilute nitric acid after washing with water, with aqueous chromic acid chemical conversion solution as the impregnation solution dipping 30-60 seconds, and then placed in the air, and finally dried by heating 50-60 deg.] C, the hot galvanized steel surface rapidly form a dense free trivalent chromate coating film, the chromic acid anodizing solution is a mixture of chromium trichloride with nitric acid, both the volume ratio is: chromium trichloride: nitric acid = 0.8 to 1.2, and a control aqueous chromic acid chemical conversion solution of at a concentration of 100-150 mg / l.
The present invention employs a mixture of chromium trichloride with nitric acid as the chemical conversion solution to promote formation of a dense hot galvanized steel surface oxide film chromic acid, chromic acid oxidation barrier film may be formed in contact with the layer of pure zinc oxyntomodulin to protect zinc, in turn, have sufficient protective potential of zinc and iron to form steel substrate, thereby further improving the corrosion resistance of galvanized steel, but also has excellent conductivity. Chromic acid and the oxide film is not carcinogenic, and in accordance with international standards SGS ROS instructions.
BRIEF DESCRIPTION
FIG chromate free coating structure 1 in FIG trivalent present invention.
Trivalent chromate FIG. 2 of the present invention changes the charge following FIG.
FIG ligand chromic acid conversion in FIG. 3 of the present invention.
Chromic acid, and hydroxide polynuclear misprinted wrong vitro hydroxide present invention. FIG. 4 is reacted FIG.
Detailed ways
The present invention provides a high corrosion resistance coating treatment method of hot galvanized steel, which is galvanized steel wire after drawing the line after the end of plating, after washing with water, dipping in dilute nitric acid, washed with trivalent chromated into the liquid immersion liquid impregnation solution as 30-60 seconds, and then placed in the air, and finally dried by heating 50-60 deg.] C, the hot galvanized steel surface rapidly form a dense coating of trivalent chromium free, trivalent chromium chemical conversion of the fluid is chromium trichloride with nitric acid mixture, the volume ratio of the two is: chromium trichloride: nitric acid = 0.8 to 1.2, and continually adding to the impregnating solution in chromic acid chemical conversion solution of chromic acid in order to control concentration of the aqueous solution into 100-150 ml / liter.
The present invention is a trivalent chromate coating film is formed as the reaction mechanism: free chromate film configuration 1) a trivalent: chromic acid type electron configuration of d (2) sp (3), is formed having six water molecules compound misalignment (FIG. 1).
2) trivalent chromate There are several variations of charge (Figure 2): [Cr (H2O) 6] (3 +) [Cr (H2O) 5X] (2+) [Cr (H2O) 4X2] ( +) [Cr (H2O) 3X3] [Cr (H2O) 2X4] (- 1) [Cr (H2O) X5] (- 2) [CrX6] (- 3) 3) chromic acid conversion ligand: ligand chromate water molecules and hydroxyl groups on the acid releases water keys, chromic two adjacent atoms combine to form polynuclear wrong, this is the conversion of water polynuclear acid group (FIG. 3).
4) These chromic hydroxide and polynuclear misprinted hydroxide reacts with the wrong vitro, the release of water, chromic acid misprinted increase, reducing the charge, the final acidified water and chromic acid chromium compound precipitates on the surface of the zinc, free chromate film is formed (FIG. 4).
The present invention is free trivalent chromate coating properties: 1, the galvanized surface of the chromate film, dehydration condensation shrinkage after drying, to form an aqueous hair corrosion resistant coating, the film thickness of chromate film is in the order of: Bright
2, where the film is exposed to physical damage zinc chromate film can be regenerated, which is a unique characteristic of the chromate film.
3, the trivalent and hexavalent chromium free chromic acid coating film, having the same corrosion resistance. Galvanized steel wire heat treatment performed after coating JIS Z2371 salt spray test results are as follows:
Such weak aqueous coating heat at 120 ℃ ~ 150 ℃, loses crystal water film, corrosion resistance decreases.
Tvrdnje (1) Sakrij zavisne prevedene s kineskog
Similar Documents
Datum izdavanja Datum izdavanja Naslov CN1263892C 2006-07-12 Sastav za obradu metalne površine i površinski obrađeni metalni materijal KR100627029B1 2006-09-21 Obrada rastvora za formiranje crne hemijske prevlake bez cinka na cink ili cinkovoj podlozi, i metoda za formiranje crne boje heksavalentna hemijska prevlaka bez hroma na podlozi koja je presvučena cinkom ili legurom cinka EP1318214B1 2010-06-23 Procesno rešenje za formiranje filmova za konverziju bez šava i bez korozije na slojevima cinkovog ili cinkovog legiranja, filmu za konverziju bez šesterobitnog hroma i korozije, formiranje istog EP1318213B1 2008-04-30 Procesno rješenje za formiranje konverzijskog filma na slojevima cinkove ili cinkove presvlake bez šupljina i otpornih na koroziju, pretvorbeni film bez šupljina i bez korozije i postupak oblikovanja istog RU2248409C1 2005-03-20 za obradu metala, metoda za proizvodnju otpornih na koroziju premaz na bazi hroma (iii) na metalnoj podlozi i artiklu koji sadrži metalni supstrat (varijante) Ramezanzadeh et al. 2010 Karakteristike korozije vruće pocinčanog čelika obrađenog različitim vrstama konverzijskih premaza JP2003171778A 2003-06-20 Metoda za oblikovanje zaštitnog filma od metala i zaštitnog filma od metala WO2005068683A1 2005-07-28 Pasivirajuća otopina bez kroma KR20100038325A 2010- 04-14 Antikorozivni tretman za slojeve konverzije CN1742114A 2006-03-01 Naknadna obrada metala presvučenih supstrata CN102268667B 2016-08-10 Trivalentni film za kemijsku pretvorbu hroma i otpornost na koroziju trivalentna otopina kemijske konverzije HU9802380A2 1999-02-01 sa fazom ponovnog ispiranja metala JP3620510B2 2005-02-16 Podloga i način njene proizvodnje i auto-dijelovi CN101184867B 2010-05-19 Kemijska tekućina za tretiranje metala i postupak obrade Yuan et al. 2010 Učinak SiO2: Na2O molarnog odnosa natrijum-silikata na otpornost na koroziju silikatnih konverzijskih premaza CN101812682A 2010-08-25 Cink-fosfatna otopina aluminija i aluminijske legure CN101029386A 2007-09-05 Trostruka kationska fosforizirajuća tekućina koja sadrži kalcij, cink i mangan obrada ploča od čelika i pocinkovane ploče CN101283117B 2013-01-02 Rješenje za tretman za formiranje crnog havalentnog filma za premazivanje bez kroma na sloju cinka ili cinka CN101316947B 2011-07-27 Površinski obrađeni čelični lim CN1158407C 2004-07-21 Chrome pasivizirajuće rješenje za zaštitu pocinčanog sloja i njegovog postupka premazivanja US2438013A 1948-03-16 Obrađeni čelični lim i postupak US5344505A 1994-09-06 Nehromni pasivizacijski postupak i sastav za pocinčane metalne površine CN1890402B 2012-05-23 Tekući trovalentni hromat za aluminijum ili legura aluminijuma i metoda za formiranje filma otpornog na koroziju na površini aluminijuma ili legure aluminijuma upotrebom istog JP2005248233A 2005-09-15 Sredstvo za smanjenje ukupnog koeficijenta trenja filma za rastvor za tretman tervalentnim hromatom, rešenje za tretman tervalentnim hromatom, način njegove proizvodnje, film tervalentnog hromata sa smanjenim ukupnim koeficijentom trenja i metodom proizvodnje JP4472965B2 2010-06-02 Trivalentni rastvor hromata i metoda za formiranje šestokalentnih prevlaka bez korozije otpornih na koroziju na presvlaku od legure cinka i nikla upotrebom istog
Prioritet i srodne aplikacije
Prioritetne aplikacije (1)
Datum primjene Datum prvenstva Datum podnošenja Naslov CN 200610098046 2006-11-29 2006-11-29 Postupak obrade premaza za visokokorroznu vruće pocinčanu čeličnu žicu
Aplikacije koje zahtijevaju prioritet (1)
Datum prijave Datum podnošenja CN 200610098046 2006-11-29 Postupak obrade premaza za visokokorroznu vruće pocinčanu čeličnu žicu
Pravni događaji
Datum Šifra Naziv Opis 2007-06-06 C06 Publikacija 2007-08-01 C10 Zahtev za ispitivanje supstance 2009-07-15 C02 Smatra se povlačenjem prijave patenta nakon objavljivanja (patentni zakon 2001)
Popularni tagovi: pocinčana čelična žica za proces, Kina, dobavljači, proizvođači, tvornica, izrađena u Kini